TIP STEEL : 08-B/1
CHARACTERISTICS:
• Manganese–Chrome–Silicon–Molybdenum steel with medium low Carbon content.
• Resilience after heat treatment about 25-40 J/cm2 (KCU)
• Resilience at –50°C is included between 15-25 J/cm2 (KCU)
• Hardness range is included between 48-52 HRC
ADAPTER STEEL : 09-B
CHARACTERISTICS:
• Manganese-Chrome-Molybdenum steel with medium-low Carbon content.
• Resilience after heat treatment about >35 J/cm2 (KCU)
• Hardness range is included between 40-45 HRC
Italricambi Spa Via dell'Industria, 21 - 33043 Cividale del Friuli Udine - Italy www.italricambi.it [email protected]
-------------------------------------------------------------------------------------------------------------------------------------------------------------All manufacturers’ name,numbers,symbols and descriptions are used for reference purpose only, and it is not implied that any part listed is
the product of these manufacturesrs
May 2009
ESCAVATOR ADAPTERS
OUR REF.
C86E
C86E/1
ORIGINAL
PART NR
132-4704
222-7700
A
(mm)
690
718
B
(mm)
180
190
C
(mm)
205
244
D
(mm)
82
93
G
(°)
15
8
WEIGHT
(Kg)
72,7
92,2
LONG TIP
OUR REF.
C88
ORIGINAL
PART NR
4T4702
A
(mm)
425
B
(mm)
205
C
(mm)
202
D
(mm)
180
E
(mm)
15
WEIGHT
(Kg)
40
ORIGINAL
PART NR
171-1709
A
(mm)
495
B
(mm)
215
C
(mm)
205
D
(mm)
180
E
(mm)
15
WEIGHT
(Kg)
53,3
ORIGINAL
PART NR
135-9700
A
(mm)
495
B
(mm)
215
C
(mm)
205
D
(mm)
180
E
(mm)
20
WEIGHT
(Kg)
63,8
PENETRATION PLUS TIP
OUR REF.
C88 RC
HEAVY DUTY ABRASION TIP
OUR REF.
C88 RP2
PENETRATION TIP
OUR REF.
C91
ORIGINAL
PART NR
4T4709
A
(mm)
425
B
(mm)
205
C
(mm)
205
D
(mm)
90
E
(mm)
15
WEIGHT
(Kg)
38,3
Italricambi Spa Via dell'Industria, 21 - 33043 Cividale del Friuli Udine - Italy www.italricambi.it [email protected]
-------------------------------------------------------------------------------------------------------------------------------------------------------------All manufacturers’ name,numbers,symbols and descriptions are used for reference purpose only, and it is not implied that any part listed is
the product of these manufacturesrs
May 2009
Scarica

Presentazione di PowerPoint